MQ硅树脂增强加成型室温硫化硅橡胶

黄伟　黄英　赵洪涛　余云照

摘要:研究了MQ硅树脂对加成型室温硫化硅橡胶的增强作用。结果表明,含乙烯基的MQ硅树脂对加成型室温硫化硅橡胶的增强作用明显，硅橡胶的透明性很好。硅橡胶的强度随着MQ硅树脂中乙烯基含量的增加先增加而后下降。SiH/SiCH＝CH₂(摩尔比)为1.2～1.5时，硅橡胶具有较好的力学性能。
关键词:MQ硅树脂；室温硫化硅橡胶；增强
中图分类号:TQ333.93　文献标识码:A
文章编号:1000－1255（2000）03－0170－03

Reinforcement of addition－ curing type room temperature
vulcanizing silicone rubber by MQ silicone resin

Huang Wei, Huang Ying, Zhao Hongtao and Yu Yunzhao
(Institute of Chemistry, Chinese Academy of Sciences, Beijing)

Abstract:The mechanical properties of room temperature vulcanizing silicone rubbers of addition－ curing type were improved by the MQ silicone resins containing vinyl groups. The silicone rubbers reinforced by MQ silicone resins had high transparency. The tensile strength of the silicone rubbers increased first and then decreased with increasing vinyl groups in MQ resin. The silicone rubbers had higher mechanical properties when the mole ratio of SiH to SiCH＝CH₂ was 1.2～ 1.5.
Keywords: MQ silicone resin; room temperature vulcanizing silicone rubber; reinforcement

作者简介：黄伟，博士。
黄伟（中国科学院化学研究所，北京，100080）
黄英（中国科学院化学研究所，北京，100080）
赵洪涛（中国科学院化学研究所，北京，100080）
余云照（中国科学院化学研究所，北京，100080）

参 考 文 献

1，黄伟,黄英,余云照.MQ硅树脂增强缩合型室温硫化硅橡胶[J].合成橡胶工业,1999,22(5)：281

收稿日期：1999－05－31；修订日期：1999－12－20。