单向聚酯帘线/橡胶复合材料的疲劳损伤机理

刘宇艳　万志敏　田振辉　杜星文

摘要:利用软X射线技术和扫描电子显微镜技术，研究了在周期载荷下单向聚酯帘线/橡胶复合材料的疲劳机理。结果表明，在高应力下，单向聚酯帘线/橡胶复合材料的疲劳损伤以聚酯帘线断裂为主；在中应力下，单向聚酯帘线/橡胶复合材料的疲劳损伤是逐步进行的；在低应力下，单向聚酯帘线/橡胶复合材料的疲劳损伤仅有局部的界面损伤。
关键词:聚酯；橡胶；复合材料；疲劳机理
中图分类号:TQ330.7文献标识码:B
文章编号:1000－1255(2000)04－0234－03

Fatigue damage mechanism of unidirectional polyester cord/ rubber composites under cyclic loading

Liu Yuyan　Wan Zhimin　Tian Zhenhui and Du Xingwen
（Department of Applied Chemistry,Harbin Institute of Technology,Harbin， Heilongjiang 150001）

Abstract:The fatigue damage mechanism of unidirectional polyester reinforced rubber composites was studied with soft X－ray radiography and scanning electron microscopy under cyclic loading.The results showed that the damage of rubber composites in form of fiber failure was observed at high cyclic stress level,the fatigue damage of rubber composites was progressively developed at medium cyclic stress and at low cyclic stress level only local interfacial failure was seen.
Keywords:polyester;rubber;composite;fatigue mechanism

基金项目：哈尔滨工业大学基金资助项目。
作者简介：刘宇艳，女，28岁，讲师。已发表论文18篇。
刘宇艳（哈尔滨工业大学应用化学系，黑龙江哈尔滨150001）　
万志敏（哈尔滨工业大学应用化学系，黑龙江哈尔滨150001）　
田振辉（哈尔滨工业大学应用化学系，黑龙江哈尔滨150001）　
杜星文（哈尔滨工业大学应用化学系，黑龙江哈尔滨150001）

参 考 文 献 ：

1，Math N M,Bhowmick A K,De S K.Chemical and scanning electron microscopy studies on fatigue failure of natural rubber　vulcanizates[J].Rubber Chemistry and Technology,1982,55(1):51～ 61
2，Omura N,Takahashi M,Nakamura T.The fatigue properties of silicone rubber[A].Presented at the meeting of the rubber　division[C].Washington Hilton:American Chemical Society,1990.9～ 12
3，傅政,谷恒勤,朱东兵,等.天然橡胶/顺丁橡胶共混物的动态疲劳与断裂特征[J].橡胶工业,1992,39(2)：107～110
4，Williams K R,Hannell J W,Swanson J M.Characterization of cord fatigue in tires[J].Rubber Chemistry andTechnology,1963,26(3):696～ 706
5，刘宇艳,万志敏,田振辉,等.单向聚酯帘线增强橡胶材料疲劳特性研究[J].复合材料学报,1998,15(4):97～101
6，刘宇艳.橡胶复合材料的疲劳[D].哈尔滨：哈尔滨工业大学,1998.53～57

收稿日期：1999－04－08
修订日期：1999－12－05