硫化时间及硫化体系对粘土胶热氧老化性能的影响

杨丹　敖宁建　杨世柱

　　摘要：用热空气老化试验和热分析法讨论了硫化时间和硫化体系对粘土胶热氧老化性能的影响。结果表明，粘土胶由于热氧性能敏感，在硫化曲线允许的范围内，硫化时间以20min为宜。采用有效硫化体系和半有效硫化体系硫化粘土胶可以使其具有较好的热氧老化性能。
　　关键词：粘土胶；硫化时间；硫化体系；热氧老化；耐老化性能
　　中图分类号：TQ332.5　　文献标识码：B
　　文章编号：1000－1255（2000）05－0310－03

Effect of vulcanization time and vulcanization system on thermal ageing property of clay－rubber masterbatch

Yang Dan
(Basic and Science Department,Zhanjiang Ocean University,Zhanjiang, Guangdong 524088)
Ao Ningjian
(South China Processing ,Design and Research Institute of Tropic Plants,Zhanjiang,
Guangdong 524001)
Yang Shizhu
(Chemistry Department,South China Normal University,Guangzhou,Guangdong 510631)

　　Abstract:The effect of vulcanization time and vulcanization systems on thermal ageing property of the clay－rubber masterbatch were investigated by air oven ageing test and thermal analysis.The results showed that the optimum vulcanization time of the clay－rubber masterbatch was 20 min in the range of vulcanization curve,because of its sensitivity to thermal ageing.When the clay－ rubber masterbatch was vulcanized by semi－efficient vulcanization system and efficient vulcanization system,better thermal ageing resistance could be obtained.
　　Keywords:clay－rubber masterbatch;vulcanization time;vulcanization system;thermal ageing;ageing resistance

基金项目：国家自然科学基金资助项目（5963001）；海南省自然科学基金资助项目（59601）。
作者简介：杨丹，女，1958年生，讲师，现为华南理工大学博士研究生。主要从事天然橡胶的复合及改性材料的研究工作。
杨丹（湛江海洋大学基础科学系，广东湛江524088）
敖宁建（华南热带农产品加工设计研究所，广东湛江524001）
杨世柱（华南师范大学化学系，广东广州510631）

参考文献

1，柯舍列夫ФФ,柯尔涅夫АМ,布卡诺夫АЕ.橡胶工艺学[M].江畹兰,王秀华,韩淑玉,等译.陕西:陕西科学技术出版社,1986.203
2，郑州电缆厂编.橡料配合与加工[M].北京:机械工业出版社,1983.146
3，郝立新,姚存爱.热分析法研究硫化体系对天然橡胶热稳定性的影响[J].合成材料老化与应用,1992,(1):4

收稿日期：1999－10－07