NBR/Zn(MAA)₂合金的硫化与交联

陈朝晖　 王迪珍　 罗东山　

摘　要：用硫化仪研究了NBR/Zn(MAA)₂合金的硫化特性。结果表明，随着Zn(MAA)₂用量的增大，合金的硫化速度提高，焦烧时间缩短，表观活化能下降。平衡溶胀及平衡应力-应变实验表明，NBR/Zn(MAA)₂合金的交联密度随Zn(MAA)₂用量的增大而增大。差示扫描量热分析表明合金内部发生了复杂的化学交联，同时Zn(MAA)₂均聚物与NBR交联网络互相贯穿缠结，起到了强迫相容的作用。
关键词：丁腈橡胶；甲基丙烯酸锌；合金；硫化；交联
分类号：TQ333.7　文献标识码：A
文章编号：1000-1255(2001)03-0169-03

Vulcanization and crosslinking of NBR/Zn(MAA)₂ alloy

Chen Zhaohui（College of Materials Science and Engineering, South China University of Technology,Guangzhou 510640, China）　
Wang Dizhen（College of Materials Science and Engineering, South China University of Technology,Guangzhou 510640, China）　
Luo Dongshan（College of Materials Science and Engineering, South China University of Technology,Guangzhou 510640, China）　

Abstract：The vulcanization characteristics ofNBR/Zn(MAA)₂ alloy were studied. It was foundthat the curing rate of the alloy increased, the scorchtime and the apparent activation energy of the alloydecreased with the increase of Zn(MAA)₂ loading.Swelling measurement and equilibrium stress - strainanalysis showed that the crosslinking density ofNBR/Zn(MAA) ₂ alloy increased as Zn(MAA)₂ loading increased. DSC indicated that complicatechemical crosslinking reaction occurred in the alloy.At the same time, the interpenetration and the en-tanglement of Zn(MAA)₂ homopolymer and NBRresulted in the forced compatibility of both phases.
Keywords：nitrile rubber;, zinc methacrylate; al-loy; vulcanization; crosslinking

参考文献：

［1］野村颢正,高野仁,丰田明宣.聚二甲基丙烯酸锌补强氢化丁腈橡胶的构造解析[J].日本橡胶协会志(日文),1993,66(11):830～838
［2］齐藤孝臣,浅田美佐子,西村浩一.甲基丙烯酸锌的聚合过程[J].日本橡胶协会志(日文),1994,67(12):867～871
［3］陈朝晖,王迪珍,罗东山,等.高性能NBR/Zn(MAA)2合金的研究[J].合成橡胶工业,1999,22(6):365～367
［4］陈朝晖,王迪珍,罗东山,等.NBR/Zn(MAA)2合金性能与结构的关系[J].合成橡胶工业,2000,23(2):107～110
［5］李继蓉.硫化橡胶溶胀指数(SI)测定方法的研究[J].橡胶工业,1988,35(4):276
［6］三田英介,稻垣慎二,冈本弘.活性填充剂配合氯丁橡胶的交联反应[J].日本橡胶协会志(日文),1994,67(7):516～521

收稿日期：2000年6月5日

修稿日期：2001年1月21日

出版日期：2001年5月15日