	合成橡胶工业 CHINA SYNTHETIC RUBBER INDUSTRY 2001 Vol.24 No.3 P.178-181

聚合物材料阻燃性能试验方法相关性研究进展

王正洲　范维澄　瞿保钧　

摘　要：介绍了聚合物材料阻燃性能常用的评价方法，如氧指数法、UL94法、锥型量热计法等，概述了每一种测试方法的优缺点，以及这些试验方法之间或与其他燃烧性能试验方法之间的相关性。
关键词：聚合物材料；阻燃；测试方法；相关性；综述
分类号：TQ317.4　文献标识码：A
文章编号：1000-1255(2001)03-0178-04

Study on correlation between measurements of flame retardancy ofpolymer materials

Wang Zhengzhou（State Key Lab of Fire Science, University of Science and Technology of China, Hefei 230026, China）　
Fan Weicheng（State Key Lab of Fire Science, University of Science and Technology of China, Hefei 230026, China）　
Qu Baojun（Department of Polymer Science and Engineering, University of Science and Technology of China,Hefei 230026, China）　

Abstract：Commonly used methods on the mea-surements of flame retardancy of polymeric materi-als, such as limiting oxygen index, UL 94 and conecalorimeter were reviewed with 31 references. Thecomments on each method were provided. The results obtained from different methods were com-pared and some correlations were found betweenthem.
Keywords：polymer materials; flame retardancy;measurement; correlation; review

作者简介：王正洲，男，1963年生，硕士，副研究员。从事聚合物材料的燃烧与阻燃方面的研究工作。
作者单位：王正洲（中国科技大学火灾科学国家重点实验室，安徽合肥230026）　
　　　　　范维澄（中国科技大学火灾科学国家重点实验室，安徽合肥230026）　
　　　　　瞿保钧（中国科技大学高分子科学与工程系，安徽合肥230026）　

参考文献：

［1］Fenimore C P, Martin F J. Flammahility of polymers[J]. Combustion and Flame, 1966(43): 141 ～ 145
［2］Tewarson A, Ogden S D. Fire behavior of PMMA[J]. Combustion and Flame, 1992(89): 237
［3］Hornsby P R, Mthupha A. Analysis of fire retardancy in magnesium hydroxide filled polypropylene composites[J]. Fire and Materials, 1996 (25): 347 ～ 354
［4］Cullis C F, Hirschler M M. The combustion of organic polymers [M]. Oxford: Oxford University Press, 1981. 125
［5］Cullis C F, Hirschler M M. Char formation from polyolefms:Correlation with low temperature oxygen uptake and flammability in the presence of metal-halogen systems[J]. Euro Polymer J,1984(20): 53 ～ 60
［6］Krevelen D W. Some basic aspects of flame resistance of polymeric materials [J]. Polymer, 1975 ( 16): 615 ～ 620
［7］Rietz G. Applicability of the oxygen index[J]. Plaste und Kautschuk, 1989, 36(11): 381 ～ 388
［8］Kaufman S. Flammability of polymers[A] . Bever B. Encyclopedia of materials science and engineering[C]. Oxford: Pergamon Press, 1986. 1 797
［9］Rietz. G. Influence of temperature on the oxygen index[J]. Plaste und Kautschuk, 1988, 35 (10): 386 ～ 388
［10］Ptetz G. Influence of ambient preasure and gravity on the oxygen index [ J ]. Plaste und Kautschuk, 1988, 35 ( 11 ): 4.26 ～ 4.28
［11］Rletz G. Regarding the influence of sample arrangement flow direction of the gases, burning direction and gas stream velocity on the oxygen index[J] . Plaste und Kautschuk, 1988, 35(9):351 ～ 353
［12］Wharton R K. The performance of various testing columns in small- scale horizontal burning studies[J]. Fire and Materials,1984, 8(4): 177 ～ 182
［13］WeilED. Additivity[A].KurylaWC, PapaAC. Flameretardant polymeric materials[C]. New York: Plenum, 1975. 103
［14］Granzow A, Cannelongo J F. The effect of red phosphorus on the flammability of poly(ethylene terephthalate) [J]. J Appl Poly Sci, 1982(20): 689 ～701
［15］Antia F K, Cullis C F, Hirschler M M. Comprehensive studies of the effect of composition on the flame- retardant activity of antimony oxide and halogenated hydrocarbons in thermoplastic polymers[J]. Euro Polymer J, 1982(18): 95 ～ 107
［16］Wharton R K. Correlation between the critical oxygen index test and other fire tests[J]. Fire and Materials, 1981, 5(3): 93 ～ 102
［17］Camino G, Costa L, Casorati E, et al. The oxygen index method in fire retardance studies of polymeric materials[J] . J Appl Polym Sci, 1988(35): 1 863 ～ 1 876
［18］Arcand C G, Vullo W J. The bottom ignition oxygen index test [J]. Text Res J, 1972(6): 328 ～ 330
［19］Jakes K A, Smith B F, Spivak S M. A modified bottom ignition oxygen index test for determination of the flammability of sewing threads[J]. Text Res J, 1974(5): 398 ～409
［20］Babrauskas V. Development of cone calorimeter NBSIR 82- 2611 [M]. Gaitherburg: US Bureau of Standards, 1982
［21］Huggett C. Estimation of rate of heat release by means of oxygen consumption measurements[J]. Fire and Materials, 1980(4):61 ～ 65
［22］Babrauskas V, Grayson S J. Heat release in fires[M]. London:Elsevier, 1992. 461
［23］Hirschler M M. How to measure smoke obscuration in a manner relevant to fire hazard assessment: Use of heat release calorimetry test equipment[J]. J Fire Sci, 1991 (9): 183 ～ 222
［24］Scudamore M J, Briggs P J, Prnger F H. Cone calorimetry－A review of tests carried out on plastics for the Association of Plastics Manufacturers in Europe[J]. Fire and Materials, 1991 (15):65 ～84
［25］王正洲,范维澄,瞿保钧,等.含氢氧化镁的阻燃硅烷交联聚乙烯U].功能高分子学报,2000,13(1):77～80
［26］Pagliari A, Cicchetti O, Bevilaequa A, et al. Flame retardants ′92[M]. London: Elsevier, 1992.41 ～ 52
［27］Molesky F. The investigation of flame retardant and smoke properties of EVA using halogenated and nonhalogenated flame retardants with the use of the cone calorimeter[M]. Proceedings of Intefflam ′90, 1990. 371 ～ 378
［28］Rychly J, Costa L. Modelling of polymer ignition and burning adopted for cone calorimeter measurements: The correlation between the rate of heat release and oxygen index[J]. Fire and Materials, 1995(19): 215 ～ 220
［29］ASTM E 1354－92, Standard test method for heat and visible smoke release for materials and products using an oxygen depletion calorimeter[S]
［30］ASTE 662－83, Standard test method for specific opticaldensity of smoke generated by solid materials[S]
［31］Foley M, Drysdale D. Note: Smoke measurement and the conecalorimeter[J]. Fire and Materials, 1994( 18): 385 ～ 387

收稿日期：2000年5月22日

修稿日期：2000年12月18日

出版日期：2001年5月15日