	合成橡胶工业 CHINA SYNTHETIC RUBBER INDUSTRY 2006 Vol.29 No.2 P.96-99

聚苯乙烯/聚丙烯酸丁酯自交联胶乳互穿聚合物网络的力学性能和动态力学性能

晏欣　孙卫红　饶秋华　

摘　要：采用种子乳液聚合制备了聚苯乙烯/聚丙烯酸丁酯自交联胶乳互穿聚合物网络.拉伸实验结果表明,用双丙酮丙烯酰胺和己二酸二酰肼自交联的胶乳互穿聚合物网络(LIPN)比相应的胶乳互穿聚合物网络具有较高的拉伸强度,并且随双丙酮丙烯酰胺用量的增加,拉伸强度增加以及永久变形降低,但离子键和氢键交联的LIPN具有很高的扯断伸长率和很大的永久变形,这些说明用双丙酮丙烯酰胺和己二酸二酰肼界面共价键交联能很好地改善力学性能和抗蠕变性能.动态力学谱结果表明,用双丙酮丙烯酰胺和己二酸二酰肼交联的LIPN比相应的LIPN以及离子键和氢键交联的LIPN具有较好的组分相容性和阻尼性能.
关键词：自交联;胶乳互穿聚合物网络;拉伸性能;动态力学谱;聚苯乙烯;聚丙烯酸丁酯
分类号：TQ316.6 　文献标识码：B
文章编号：1000-1255(2006)02-0096-04

Mechanical and dynamic mechanical properties of self-crosslinkable latex interpenetrating polymer network based on polystyrene and poly(butyl acrylate)

Yan Xin（Department of Chemistry and Material,Naval University of Engineering,Wuhan 430033,China）　 Sun Weihong（Department of Chemistry and Material,Naval University of Engineering,Wuhan 430033,China）　 Rao Qiuhua （Department of Chemistry and Material,Naval University of Engineering,Wuhan 430033,China）　

Abstract：Self-crosslinkable latex interpenetrating polymer network (LIPN) based on polystyrene and poly(butyl acrylate) was prepared by seed emulsion polymerization. The results of tension tests showed that the LIPN crosslinked with diacetone acrylamide and adipyl dihydrazide had higher tensile strength than that of the corresponding latex interpenetrating polymer network and their tensile strength increased and permanent sets decreased with increasing the content of diacetone acrylamide, but the LIPN crosslinked by hydrogen and ionic bonds had much higher elongation at break and permanent set. These suggested that the interfacial covalent-bond crosslinked with diacetone acrylamide and adipyl dihydrazide could obviously improve mechanical and creep-resistant properties. The results of dynamic mechanical spectra showed that the self-crosslinkable LIPN crosslinked with diacetone acrylamide and adipyl dihydrazide had much more component compatibility and damping properties than the corresponding LIPN and the LIPN crosslinked by hydrogen and ionic bonds.
Keywords：self-crosslinking; latex interpenetrating polymer network; tensile property; dynamic mechanical spectrum; polystyrene; poly(butyl acrylate)

作者简介：Yan Xin,doctor,professor.
作者单位：晏欣（海军工程大学,化学与材料系,湖北,武汉,430033）　
　　　　　孙卫红（海军工程大学,化学与材料系,湖北,武汉,430033）　
　　　　　饶秋华（海军工程大学,化学与材料系,湖北,武汉,430033）　

参考文献：

[1]Sperling L H.Interpenetrating polymer networks and related materials[M].Beijing:Science Press,1987.6～8
[2]Kim S C,Klempner D E,Frisch K C,et al.Polyurethane-polystyrene interpenetrating polymer networks[J].Polym Eng Sci,1975,15(5):339～342
[3]Grates J A,Thomas D A,Hickey E C,et al.Noise and vibration damping with latex interpenetrating polymer networks[J].J Appl Polym Sci,1975,19(6):1 731～1 743
[4]Foster J N,Sperling L H,Thomas D A.The applications of bulk polymerized acrylic and methacrylic interpenetrating polymer networks to noise and vibration damping[J].J Appl Polym Sci,1987,33(7):2 637～2 645
[5]Chang M C,Thomas D A,Sperling L H.Sound and vibration damping with IPN[J].J Polym Mater,1989,6(2):61～72
[6]Yao Shuren.Means to widen the temperature range of high damping behavior by IPN formation[A].In:Klempner D,Frisch K C.Interpenetrating Polymer Networks (Ⅳ)[M].Lancaster:Technomic Publ,1994.243～286
[7]Yan Xin,Yao Shuren,Zhang Baozhen,et al.Studies of the damping materials based on latex interpenetrating polymer networks of poly(methyl methacrylate) and poly(butyl acrylate)[J].Chin Polym Mater Sci Eng,1994,10(3):80～83
[8]Wang Jingyuan,Liu Ruiying,Li Weihua,et al.Studies on the damping performance of polystyrene/polyacrylate latex IPN[J].Polym Intern,1996,39(2):101～104
[9]Hu R,Dimonie V L,El-Aasser M S,et al.Multicomponent latex IPN materials (2):Damping and mechanical behavior[J].J Polym Sci:Polym Phys,1997,35(10):1 501～1 514
[10]Manoj N R,Chandrasekhar L,Patri M,et al.Vibration damping materials based on interpenetrating polymer networks of carboxylated nitrile rubber and poly(methyl methacrylate)[J].Polymers for Advanced Technologies,2002,13(9):644～648
[11]Silverstein M S,Narkis M.Capillary extrusion of elastomeric emulsion crosslinked interpenetrating networks[J].Polym Eng Sci,1985,25(5):257～263
[12]Nemirovski N,Silverstein M S,Narkis M.Latex interpenetrating polymer networks:From structure to properties[J].Polym Adv Technol,1996,7(4):247～256
[13]Yoo S,Harelle L,Daniels E S,et al.Interfacial aspects of strength development in poly(methyl methacrylate) based latex systems[J].J Appl Polym Sci,1995,58(2):367～374
[14]He Y,Daniels E S,Klein A,et al.Elastomeric films from structured latexes[J].J Appl Polym Sci,1997,64(6):1 143～1 152
[15]Yan Xin,Meng Jinfeng,Yao Shuren.Study on the damping materials based on interfacial crosslinking latex interpenetrating polymer networks of poly(methyl methacrylate) and poly(butyl acrylate-co-acrylic acid)[J].China Elastomerics,2002,12(1):31～34
[16]Narkis M,Talmon Y,Silverstein M S.Properties and structure of elastomeric two-stage emulsion interpenetrating networks[J].Polym,1985,26(9):1 359～1 364
[17]Silverstein M S,Narkis M.Elastomeric domain-type interpenetrating polymer networks[J].J Appl Polym Sci,1987,33(7):2 529～2 547

收稿日期：2005年2月1日

出版日期：2006年3月15日

请看PDF全文