合成橡胶工业 |
![]() |
|
不同注射条件对尼龙6力学性能的影响 赵树高 郑韦 尹兴昌 Sonja Pongratz 摘 要:考察了尼龙6在3种不同注射机参数和注射机不同部位分别充满氩气的条件下进行注射对其力学性能的影响.结果表明,尼龙6在240 ℃、转子转速127 r/min及氩气氛围内能够大幅度提高其力学性能.尼龙6原材料颗粒中存在的氧气是其生产过程中氧化降解的主要原因,注射之前在氩气条件下干燥能够提高产品的力学性能. Influence of injection conditions on mechanical performance of polyamide-6 Zhao Shugao(Key Laboratory of Rubber-Plastics of Ministry of Education, Qingdao University of Science and Technology, Qingdao 266042, China) Zheng Wei(Key Laboratory of Rubber-Plastics of Ministry of Education, Qingdao University of Science and Technology, Qingdao 266042, China) Yin Xingchang(Key Laboratory of Rubber-Plastics of Ministry of Education, Qingdao University of Science and Technology, Qingdao 266042, China) Sonja Pongratz(Lehrstuhl für Kunststofftechnik , University of Erlangen-Nurnmberg University, Erlangen 91058, Germany) Abstract:Some tests were done to polyamide-6 (PA 6) injected in three different settings of injection machine and inert atmosphere full of different sections.The results showed that PA 6 which was injected with screw speed 127 r/min and 240 ℃ in argon had an improvement of mechanical performance.The presence of oxygen within granule material played an important role during the oxidative degradation.Drying material in the argon before injection was a good method to improve the mechanical performance of production. |
参考文献:
[1]Pongratz S,Montagne F D,Ehrenstein G.Influence of processing on the degradation of PA and PP[J].Kunstst Plast Eur,2000,90(2):301~303
[2]Sierra F.Influence of the processing parameters on the thermal-oxidative and hydrolytic long-term stability by the example of the pipe extrusion of PA 66[D].Germany:Institute of Polymer Technology,University of Erlangen-Nuernmberg University,2003
[3]Cerruti P,Carfagna C,Rychly J,et al.Chemiluminescence from oxidation of polyamide 6[J].Polym Degra Stab,2003,82(3):477~485
[4]Herrera M,Matuschek G,Kettrup A.Main products and kinetics of the thermal degradation of polyamides[J].Chemosphere,2001,42(5~7):601~607
[5]Villain F,Coudane J,Vert M.Thermal degradation of poly(ethylene terephthalate) and the estimation of volatile degradationproducts[J].Polym Degra Stab,1994,43(3):431~440
[6]Montagne F D,Pongratz S,Ehrenstein G.Studies of the thermal and thermooxidative degradation of polypropylene during processing and usage[C].ANTEC,New York,1999
[7]Müller N,Ehrenstein G W.Mechanical performance of polymerafter screw plastication in inert atmosphere[C].SPME Conference Proceedings,Qingdao,2002
[8]Schieblisch J,Ehrenstein G W.Recycling of polyamide 6:Effect of contaminats[C].ANTEC,Boston,1995
收稿日期:2005年3月10日 出版日期:2006年5月15日 |