三元乙丙橡胶挤出压力振荡现象的影响因素

张娜　 赵贝　 王宁　 曲德金　 吴其晔　

摘　要：采用恒速型双筒毛细管流变仪研究了剪切速率、口模温度和含氟弹性体偏氟乙烯-六氟丙烯-四氟乙烯共聚物(PPA)对三元乙丙橡胶(EPDM)挤出压力振荡现象的影响.结果表明,EPDM高速挤出时,升高温度可以推迟挤出压力振荡现象的发生;振荡周期和振幅均随剪切速率的增加而减小;加入PPA可以改善EPDM挤出物的外观,且挤出压力低于纯EPDM,PPA质量分数越大,其降低幅度越大.
关键词：三元乙丙橡胶;双筒毛细管流变仪;挤出压力振荡
分类号：TQ333.4 　文献标识码：B
文章编号：1000-1255(2009)03-0219-04

Effect factors on extrusion pressure oscillation phenomena of ethylene-propylene-diene rubber

Zhang Na（Key Laboratory of Rubber-Plastics of Ministry of Education,Qingdao University of Science and Technology,Qingdao 266042,China）　 Zhao Bei（Key Laboratory of Rubber-Plastics of Ministry of Education,Qingdao University of Science and Technology,Qingdao 266042,China）　 Wang Ning（Key Laboratory of Rubber-Plastics of Ministry of Education,Qingdao University of Science and Technology,Qingdao 266042,China）　 Qu Dejin（Key Laboratory of Rubber-Plastics of Ministry of Education,Qingdao University of Science and Technology,Qingdao 266042,China）　 Wu Qiye （Key Laboratory of Rubber-Plastics of Ministry of Education,Qingdao University of Science and Technology,Qingdao 266042,China）　

Abstract：The influences of shear rate,die temperature,fluoroelastomer vinylidene fluoride-hexafluoropropylene-tetrafluoroethylene copolymer (PPA) on the extrusion pressure oscillation phenomena of ethylene-propylene-diene rubber (EPDM) were systematically studied through a double capillary rheometer.The results showed that the extrusion pressure oscillation phenomena of EPDM was delayed with increasing temperature at high speed extrusion,the pressure oscillation period and the amplitude were decreased with the increase of shear rate.The appearance quality of EPDM melt was improved with adding PPA.The extrusion pressure was lower than that of pure EPDM,and its decreasing range was larger with increasing mass fraction of PPA.
Keywords：ethylene-propylene-diene rubber;double capillary rheometer;extrusion pressure oscillation

基金项目：国家自然科学基金资助项目(50573037;50390090).
作者简介：张娜(1983-),女,硕士.已发表论文10余篇.
作者单位：张娜（青岛科技大学,橡塑材料与工程教育部重点实验室,山东,青岛,266042）　
　　　　　赵贝（青岛科技大学,橡塑材料与工程教育部重点实验室,山东,青岛,266042）　
　　　　　王宁（青岛科技大学,橡塑材料与工程教育部重点实验室,山东,青岛,266042）　
　　　　　曲德金（青岛科技大学,橡塑材料与工程教育部重点实验室,山东,青岛,266042）　
　　　　　吴其晔（青岛科技大学,橡塑材料与工程教育部重点实验室,山东,青岛,266042）　

参考文献：

[1]Herwing J,Kaminsky W.Halogenfree soluble Ziegler catalysts with methylalumoxane as cocatalyst[J].Polym Bull,1983,9(2):464-467.
[2]吴其哗,巫静安.高分子材料流变学[M].北京:高等教育出版社,2002:173-207.
[3]张娜,王宁,赵贝,等.限定几何构型茂金属催化聚烯烃弹性体EPDM Nordel IP的高速流变性能[J].弹性体,2008,18(1):4-9.
[4]吴其晔,慕晶霞,张娜,等.含氟弹性体对聚烯烃熔体高速挤出性能的影响[C]//2007年全国高分子学术论文报告会论文报告会论文摘要集.成都:中国化学会,2007:310-314.

收稿日期：2008年3月12日

修稿日期：2009年2月22日

出版日期：2009年5月15日

请看PDF全文