合成橡胶工业090408-橡胶技术网 www.sto.net.cn

	合成橡胶工业 CHINA SYNTHETIC RUBBER INDUSTRY 2009 Vol.32 No.4 P.293-297

氟橡胶/环氧丙烯酸酯橡胶共混物的双连续相形态和性能

陈春明　熊传溪　

摘　要：采用双螺杆挤出机,通过熔融共混法制备了氟橡胶(FKM)/环氧丙烯酸酯橡胶(EACM)共混物.用透射电镜和动态机械热分析仪研究了FKM/EACM共混物的形态、热力学性能和动态机械性能,探讨了共混比对其力学性能的影响.透射电镜研究结果显示,FKM/EACM共混物在共混比范围内呈现出完美的两相连续结构形态,共混体系的相畴尺寸随着EACM用量的不同而改变,当FKM/EACM(质量比)为80/20时,EACM在FKM的基质中形成最完善的网络结构;同时两相产生了协同效应,FKM/EACM共混物的拉伸强度和撕裂强度达到最大值.
关键词：氟橡胶;环氧丙烯酸酯橡胶;共混;网络结构;机械性能
分类号：TQ333.93 　文献标识码：A
文章编号：1000-1255(2009)04-0293-05

Co-continuous phase morphology and properties of fluoroelastomer/epoxy acrylate elastomer blends

Chen Chunming（Department of Chemistry,Hanshan Normal University,Chaozhou 521041,China）　 Xiong Chuanxi（School of Materials Science and Engineering,Wuhan University of Technology,Wuhan 430070,China）　

Abstract：Fluoroelastomer(FKM) and epoxy acrylate elastomer(EACM) blends were prepared by melt blending through a twin-screw extruder. Morphology, thermal properties, dynamic mechanical properties were investigated and confirmed by transmission electron microscopy (TEM) and dynamic mechanical thermal analysis. The effects of the composition ratios on mechanical properties were studied. TEM showed that FKM/EACM blends exhibited a perfect co-continuous phase structure in a limited range of blending ratio, where EACM formed a network in FKM matrix. The morphology of FKM/EACM blends demonstrated a different network size with the change of EACM amount. A fine and complete network structure of EACM in FKM matrix was achieved at the mass ratio of FKM/EACM 80/20. Mechanical testing indicated a synergistic effect at the FKM/EACM 80/20 with maximal values for both the tensile strength and the tear strength.
Keywords：fluoroelastomer; epoxy acrylate elastomer; blend; networks structure; mechanical property

基金项目：Supported by Natural Science Foundation of Guangdong Province(7301526).
作者简介：Chen Chunming,doctor,vice-professor
作者单位：陈春明（韩山师范学院,化学系,广东,潮州,521041）　
　　　　　熊传溪（武汉理工大学,材料科学与工程学院,湖北,武汉,430070）　

参考文献：

[1]Sabbagh S H E.Compatibility study of natural rubber and ethylene-propylene diene rubber blends[J].Polymer Testing,2003,22(1):93-100.
[2]Wootthikanokkhan J,Tunjongnawin P.Investigation of the ef-fect of mixing schemes on cross-link distribution and tensile properties of natural-acrylic rubber blends[J].Polymer Testing,2003,22(3):305-312.
[3]Ghosh A,Naskar A K,Khastgir D,et al.Dielectric properties of blends of silicone rubber and tetraflouroethylene/propylene/vinylIDene fluorIDe terpolymer[J].Polymer,2001,42(24):9849-9853.
[4]Dong Hwee Kim,Jisu Choi,Young Taik Hong,et al.Phase separation and morphology control of polymer blend membranes of sulfonated and nonsulfonated polysulfones for direct methanol fuel cell application[J].Journal of Membrane Science,2007,299(1):19-27.
[5]Eduardo D R,Nash J M,Williams J C,et al.Co-continuous composites for high-temperature applications[J].Materials Science and Engineering,2007,463(1):115-121.
[6]Omonov T S,Harrats C,Groeninckx G.Co-continuous and encapsulated three phase morphologies in uncompatibilized and reactively compatibilized polyamIDe 6/polypropylene/polystyrene ternary blends using two reactive precursors[J].Polymer,2005,46(26):12322-12336.
[7]Elmér A M,Jannasch P.Gel electrolyte membranes derived from co-continuous polymer blends[J].Polymer,2005,46(19):7896-7908.
[8]Kenta Suzuki,Hiromu Saito,Masatoshi Tokita,et al.Development of co-continuous structure in liquID crystalline polyester[J].Polymer,2005,46(19):8313-8320.
[9]Sarazin P,Roy X,Favis B D.Controlled preparation and properties of porous poly(L-lactIDe) obtained from a co-continuous blend of two biodegradable polymers[J].Biomaterials,2004,25(28):5965-5978.
[10]Riscanu D,Favis B D,Feng Chaoyang,et al.Thin-film membranes derived from co-continuous polymer blends:Preparation and performance[J].Polymer,2004,45(16):5597-5609.
[11]Yuan Zhenhua,Favis B D.Macroporous poly(L-lactIDe) of controlled pore size derived from the annealing of co-continuous polystyrene/poly(L-lactIDe) blends[J].Biomaterials,2004,25(11):2161-2170.
[12]Mathew A P,Packirisamy S,Radusch H J,et al.Effect of initiating system,blend ratio and crosslink density on the mechanical properties and failure topography of nano-structured full-interpenetrating polymer networks from natural rubber and polystyrene[J].Eur Polym J,2001,37(9):1921-1934.
[13]Marin N,Favis B D.Co-continuous morphology development in partially miscible PMMA/PC blends[J].Polymer,2002,43(17):4723-4731.
[14]Chen Chunming,Xiong Chuanxi,Dong Liji,et al.Synthesis of acrylate elastomer with aether group and modification for flouroelastomer[J].合成橡胶工业,2006,29(4):271-274.

收稿日期：2008年6月4日

出版日期：2009年7月15日

请看PDF全文