弹性体
CHINA ELASTOMERICS
2000　Vol.10　No.2　P.7-9

充油溶液聚合丁苯橡胶的研究

薛宏 　计福春　张春庆　穆瑞凤　李伟　刘青

　　摘要：以多螯锂作引发剂，用阴离子聚合方法合 成了支化溶液聚合丁苯橡胶，并采用湿法充 油技术制备了充油溶聚丁苯橡胶。结果表明：聚合体系内DVB用量增加，多螯引发剂相对分 子质量分布逐渐加宽，支化程度逐渐增大，用该法制得的充油溶聚丁苯橡胶物理机械力学性 能优异。
　　关键词：丁二烯；苯乙烯；阴离子聚合；多螯引发剂；充油
　　中图分类号：TQ0631.5　　文献标识码：A　　文章编号：1 005-3174(2000)02-0007-03

The study on oil-extended S-SBR

XUE Hong,JI Fu-chun,ZHANG Chun-qing,MU Rui-feng
（College of Chemical Engineering,Dalian University of Technology ,Dalian　11601 2，China）
LI Wei,LIU Qing
（Research Institute of Beijing Yanshan Petrochemical Corporation,Beij ing　102550，China）

ABSTRACT

　　In this paper,DVB was first polymerized with butadiene using butyllithium in cyc lohexane to form soluble multi melic initiator.After the completion of copolymer ization of butadiene and styrene with this kind of initiator,a kind of branchin g structure SSBR was obtained.Mixing the polymer solution with aromatic oil or na phthenic oil,the oil-extended SSBR could be prepared.It was shown that values o f MWD were increased with the increase of mole ratio of ［DVB］／［n-BuLi］,an d prepared oil-extended SSBR had excellent mechanical properties.
　　Key words:butadiene;styrene;anionic polymerization;multi melic initiator;oil extended

作者简介：薛宏(1969－)，男，吉林省长春市人，讲师，博士，主要从事新型弹性体及活性 聚合研究。
薛宏（大连理工大学化工学院高分子材料系，辽宁大连　116012）
计福春（大连理工大学化工学院高分子材料系，辽宁大连　116012）
张春庆（大连理工大学化工学院高分子材料系，辽宁大连　116012）
穆瑞凤（大连理工大学化工学院高分子材料系，辽宁大连　116012）
李伟（北京燕山石油化工公司研究院，北京　102550）
刘青（北京燕山石油化工公司研究院，北京　102550）

参考文献：
［1］　H.D.Harington,K.V.Weinstock,The Production and utilization of High moon ey viscosity Synthetic Rubber－Ⅰ［J］.India Rubber world,1951,124(4):435-442.
［2］　H.D.Harington,K.V.Weinstock,The Production and utilization of High mooney viscosity Synthetic Rubber－Ⅱ［J］.India Rubber world,1951,124(5):571－575.
［3］　刘大华.合成橡胶工业手册［M］.北京：化学工业出版社，1990.349.

收稿日期：2000－02－02