镍系充油顺丁橡胶BR9073的工业技术开发

刘同金　张金萍

　　摘要：在万吨级顺丁装置上，采用加入D组分的Ni－Al－B催化体系及湿法间断充油工艺进行了镍系充油顺丁橡胶BR9073的试生产。工业试验结果表明：现有顺丁胶生产装置适宜，聚合胶液门尼可调性强，n(Al)／n(B)调节范围为0.5～1.1；生产过程中因胶液动力粘度大，输送困难，可适当充溶剂油加以解决；溶剂油系统可与顺丁胶共用；所得产品的宏观及微观质量均达到国外同类产品水平。
　　关键词：充油；顺丁橡胶；镍系催化剂；工业试验
　　中图分类号：TQ333.2　　文献标识码：A　　文章编号：1005-3174(2000)04-0001-04

The development of Ni-family oil-extended polybutadiene
rubber BR9073 in industrial production

LIU Tong-jin　ZHANG Jin-ping
(Synthetic Rubber Plant of Qilu Petrochemical Co.,Ltd.,Zibo　255438,China)

ABSTRACT　The industrial trial-production of Ni-family oil-extended polybutadiene rubber BR9073 was carried out by adding D component into the Ni-Al-B catalytic system and using the wet process of batch oil-extending on the plant with its annual BR output capacity of ten thousands tons.the result of industrial experiment showed that the BR plant is proper for OE BR production,the Mooney viscosity of the polymer solution is controllable on a greater extent,the ratio of Al／B can be adjusted from 0.5 to 1.1,greater dynamic viscosity resulting conveying problems cab be solved by adding solvelt oil in the process,the solvent oil system cab be shared with the BR production and the quality of the product obtained matches that of foreign product of the same type both in macrostructure and microstructure.
Keywords:oil-extended;polybutadiene rubber;Ni-family catalyst;industrial experiment

基金项目：中国石油化工总公司科研项目(合同号：297020)。
作者简介：刘同金(1962－)，男，高级工程师，获中国石油化工总公司科技进步三等奖1项。已发表论文2篇。
刘同金（齐鲁石化股份公司橡胶厂，山东 淄博　255438）
张金萍（齐鲁石化股份公司橡胶厂，山东 淄博　255438）

参　考　文　献：
［1］　范汝良.芳烃油用量对充油镍系BR性能的影响［J］.合成橡胶工业，1992，15(2)：81－84.
［2］　武玉斌.高芳烃油填充镍系顺丁橡胶的性能［J］.合成橡胶工业，1994，17(6)：362－364.
［3］　高明献，李迎.充油顺丁胶生产中溶剂油的循环利用［J］.齐鲁石油化工，1993，21(2)：127.
［4］　李迎，高明献，张允武，等.聚合温度对Ni(Naph)₂－Al(i－Bu)₃－BF₃.OEt₂－O体系合成顺丁胶的影响［J］.齐鲁石油化工，1992，20(2)：117.
［5］　魏如冰，陈铃山.高门尼顺丁橡胶湿法连续充油试验［J］.齐鲁石油化工，1994，22(4)：314.
［6］　傅彦杰，赵振华，翁锁海，等.镍系充油BR的基本性能试验研究［J］.橡胶工业，1999，46(1)：16－25.

收稿日期：2000-06-07