2000 Vol.47 No.11 P.647-651

 橡胶技术网

新型无机纳米填料对SBR的补强性能

贾红兵　 金志刚　 吉庆敏　 胡国林　 张士齐　

摘　要：研究了纳米白炭黑、纳米二氧化钛、纳米氧化铝和白炭黑分别与炭黑并用对SBR的补强性能，并与单独填充炭黑进行了对比。试验结果表明，纳米白炭黑／炭黑并用体系能够显著提高SBR硫化胶的拉伸性能、热氧老化性能和疲劳性能，而纳米氧化铝／炭黑和纳米二氧化钛／炭黑并用体系能够提高SBR硫化胶的耐磨性。
关键词：纳米粒子；炭黑；SBR；物理性能；疲劳性能；耐磨性
分类号：TQ330.38　文献标识码：B
文章编号：1000-890X(2000)11-0647-05

Reinforcement of nano-fillers to SBR

JIA Hong-bing ,JIN Zhi-gang ,JI Oing-min ,HU Guo-lin ,ZHANG Shi-qi
(anjing University of Science and Technology,Nanjing 210094,China)

Abstract：The reinforcements of nano-silica/carbon black,nano-titanium dioxide/carbon black,nano-aluminum oxide/carbon black and silica/carbon black respectively to SBR were investigated and compared to that of carbon black alone.The results showed that the tensile strength,thermo-oxidative aging property and fatigue property of SBR vulcanizate were significantly improved by using nano-silica/carbon black;the abrasion resistance of SBR vulcanizate was improved by using nano-aluminum oxide/carbon black or nano-titanium dioxide/carbon black.
Keywords：nano-particle;carbon black;SBR;fatigue property;abrasion resistance

基金项目：国家自然科学基金资助项目(27674013)
作者简介：贾红兵(1967-)，女，江苏扬州人，南京理工大学讲师，博士，主要从事高分子材料方面的教学与科研工作。
作者单位：贾红兵（南京理工大学高分子材料系，江苏 南京 210094）　
　　　　　金志刚（南京理工大学高分子材料系，江苏 南京 210094）　
　　　　　吉庆敏（南京理工大学高分子材料系，江苏 南京 210094）　
　　　　　胡国林（南京理工大学高分子材料系，江苏 南京 210094）　
　　　　　张士齐（南京理工大学高分子材料系，江苏 南京 210094）　

参考文献：

［1］胡伯顺．现代科学仪器——纳米科技及检测仪器专辑[M]．北京：现代科学仪器编辑部，1988．5-34．
［2］张立德，牟其美．纳米材料学[M]．沈阳：辽宁科技出版社，1999．32．
［3］Wacner M P.Reinforcing silicas and silicates[J].Rubber Chemistry and Technology,1976,49(3):703.
［4］藤本邦彦．ゴ厶の不均质构造たふびに疲劳现象[J]．日本ゴ厶写协会誌，1964，37(8)：602．

收稿日期：2000-07-26

请看PDF全文