活性剂FT对NR和BR及SBR胶料性能的影响

刘军　 侯新锋　 仇轩　

摘　要：研究了橡胶活性剂FT与氧化锌不同并用比对NR，BR和SBR胶料硫化特性和硫化胶物理性能的影响。试验结果表明，在NR和BR及SBR胶料配方中活性剂FT可以等量替代40％～60％的氧化锌(即活性剂FT／氧化锌的最佳并用比为2．0／3．0～3．0／2．0)，而胶料的硫化特性基本保持不变，硫化胶物理性能稍有改善。
关键词：活性剂；NR；BR；SBR；硫化特性；物理性能
分类号：TQ330．38+7　文献标识码：B
文章编号：1000-890X(2000)12-0720-03

Influence of activator FT on properties of NR, BR and SBR compounds

LIU Jun ,HOU Xin-feng ,QIU Xuan
(South China University of Technology, Guangzhou 510641, China)

Abstract：The influence of activator FT/ZnO blending ratio on the curing behavior of NR, BR and SBR compounds and the physical properties of their vulcanizates was investigated. The test results showed that the curing behavior of the compounds changed little, and the physical properties of their vulcanizates improved slightly by replacing 40%～60% of ZnO with the same amount of FT in NR,BR and SBR compounds respectively.
Keywords：activator; NR; BR; SBR; curing behavior; physical properties
作者简介：刘军(1944-)，女，山东荣成人，华南理工大学材料学院副教授，主要从事聚合物及胶粘剂方面的研究工作。
作者单位：刘军（华南理工大学材料学院，广东广州 510640）　
　　　　　侯新锋（华南理工大学材料学院，广东广州 510640）　
　　　　　仇轩（华南理工大学材料学院，广东广州 510640）　

参考文献：

［1］朱 彤．活性剂FT在自行车内胎中的应用[J]．橡胶工业，1998，45(11)：672～673．

收稿日期：2000-06-16

请看PDF全文