硫黄硫化的异戊二烯橡胶在超临界二氧化碳中的脱硫作用

胡小龙　

摘　要：本文研究了一种新型的脱硫工艺,该工艺采用脱硫试剂在超临界二氧化碳中使橡胶脱硫.首先,通过控制硫化时间和硫化剂,制备具有不同交联状态的无填料聚异戊二烯橡胶试样(硫化制品).每一种所用的硫化胶都采用丙酮和氯仿的共沸物通过索氏抽提法除去残余硫化剂.然后在超临界二氧化碳存在下在不同的温度下(140～200℃)脱硫60分钟.制品被分馏成溶胶和凝胶组分,并且测试了溶胶组分的分子量和凝胶组分的交联密度.实验显示,在所用的几种脱硫试剂中,硫醇胺的效果较好;其脱硫产生的溶胶组分的分子量大约为10000,而凝胶组分的交联密度则与初始值相比显著降低.随着二氧化碳压力的增大,溶胶组分的得率相应增大.在超临界液体二氧化碳中,硫化制品的脱硫效果比在常规的气体二氧化碳中更佳.获得溶胶的比率在相当大程度上依赖于硫化胶的交联状态.上述结果说明,在超临界二氧化碳存在的条件下,脱硫试剂穿透了硫化胶并在其内部得到了较好的分散.

参考文献：

[1]W.E.Stafford and R.A. Wright; Rubber. Technol 31,599(1958)
[2]D.s. LE Beau; Rubber Chem. Technol. 40,217(1967)
[3]N. Kavabata, K. Mori, T. Fujii, and S. Yamashita; Nippon Gomu Kyokaisi 49,298 (1976) and the following papers in the same journal.
[4]H. Okamoto, S. Inagaki, Y. Onouti, and J. Furukawa;Nippon Gomu Kyokaisi; 52,774(1979)
[5]P.P. Nicholas, Rubber Chem. Technol. 55, 1499(1982)
[6]W.C. Warner, Rubber Chem. Technol. 67,559(1994)
[7]A.I. Isayev, J. Chen, and A. Tukachinsky, Rubber Chem. Technol. 68,267(1995)
[8]M. Mouri, N. Sato, and H. Okamoto,et.al, Nippon Gomu Kyokaisi 72.43(1999)
[9]B. Adhikari, D. De and S. Maiti, Prog. Polym. Sci. 25,909(2000)
[10]O. Kajimoto, S.C. Tucker, and C.J. Peters, et.al, Chem.Rev. 99,353(1999)
[11]M. Perrut, Ind. Eng. Chem. Res. 39,4531(2000)
[12]S.H. Chang, S.C. Park, and J.J. Shim, J. Supercrit.Fluids 13, 113(1998)
[13]T. Funazukuri, S. Ogasawara, and N. Wakao, et.al, J.Chem. Eng. Japan 18, 455(1985)
[14]S.B. Lee and I.K. Hong, J. Ind. Eng. Japan 18, 455(1985)
[15]J.R. Kershaw, Fuel 77, 1113(1998)
[16]J.A. Hyatt, J. Org. Chem. 49,5097(1984)
[17]P.J. Flory and J.Rehner, Jr., J. Chem. Phys. 8, 108(1950)
[18]C.J. Sheehan and A.L. Bisio, Rubber Chem. Technol.39, 149(1966)
[19]W.A. Pryor, "Mechanism of Sulfur Reaction," MCGraw-Hill, N. Y., 1962, p.60.
[20]B.Saville and A.A. Watson, Rubber Chem. Technol.40, 100(1967)
[21]Y. Onouti, S. Inagaki, and H.Okamoto, et.al., Nippon Gomu Kyokaisi 53,756(1980)
[22]A.M. Zaper and J.L. Koenig, Rubber Chem. Technol.60, 252(1987)
[23]M.L. Studebaker and L.G. Nabors, Rubber Chem. Technol.32, 941(1959)
[24]D.S. Campbell, J. Appl. Polym. Sci. 13, 1201(1969)
[25]E. Morita and E.J. Young, Rubber Chem. Technol. 36,16(1944)
[26]M.L. Selkar and A.R. Kemp, Ind. Eng. Chem. 36, 16(1944)
[27]C.G. Moore, J. Polymer Sci. 18, 503(1958)

出版日期：2005年6月1日